| 性能项目 | 测试条件 | 测试方法 | 数值/描述 | 单位 | |
| 机械性能 | 拉伸强度(引张强度) | ASTM D638/ISO 527 | 58 | kg/cm2(MPa)[Lb/in2] | |
| 断裂伸长率 | ASTM D638/ISO 527 | 4.0 | % | ||
| 拉伸模量 | ASTM D638/ISO 527 | kg/cm2(MPa)[Lb/in2] | |||
| 拉伸屈服伸长率(延伸率) | ASTM D638/ISO 527 | % | |||
| 拉伸断裂伸长率(延伸率) | ASTM D638/ISO 527 | % | |||
| 弯曲模量(弯曲弹性率) | ASTM D790/ISO 178 | 4050 | kg/cm2(MPa)[Lb/in2] | ||
| 弯曲强度 | ASTM D790/ISO 178 | 97 | kg/cm2(MPa)[Lb/in2] | ||
| 洛氏硬度 | ASTM D785 | ||||
| IZOD 缺口冲击强度 | 1/4" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | ||
| 1/4" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" 23℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 1/8" -30℃ | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| Charpy冲击强度 | 23℃ (缺口) | ASTM D256/ISO 179 | 2.5 | kg·cm/cm(J/M)ft·lb/in | |
| -30℃(缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 23℃(无缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| -30℃(无缺口) | ASTM D256/ISO 179 | kg·cm/cm(J/M)ft·lb/in | |||
| 物性性能 | 比重(密度) | ASTM D792/ISO 1183 | 1.64 | ||
| 成型收缩率 | ASTM D955 | 1.5 | % | ||
| 熔融指数(流动系数) | 200℃/5kg | ASTM D1238/ISO 1133 | 19 | g/10min | |
| 220℃/10kg | ASTM D1238/ISO 1133 | g/10min | |||
| 吸水率 23℃/24H | ASTM D570/ISO 62 | 0.2 | % | ||
| 热性能 | 热变形温度 | 退火 | ASTM D648/ISO 75 | ℃(℉) | |
| 未退火 | ASTM D648/ISO 75 | ℃(℉) | |||
| 维卡软化点 | ASTM D1525/ISO R306 | ℃(℉) | |||
| 熔点 | - | 165 | ℃(℉) | ||
| 燃烧性(率) | UL94 | HB | |||
| 线性膨胀系数 | ASTM D696/ISO 11359 | 9 | mm/mm.℃ | ||
| 电气性能 | 介电常数 | 100HZ | ASTM D150/IEC 60250 | 20 | |
| 1MHZ | ASTM D150/IEC 60250 | ||||
| 体积电阻率 | ASTM D257/IEC 60093 | 1x10的14次方 | Ω.cm | ||
| 表面电阻率 | ASTM D257/IEC 60093 | 1x10的16次方 | Ω | ||
| 耐电弧性 | ASTM D495/IEC 60112 | ||||
| 加工条件 | 干燥条件 | 80-100C(175-210F),3-4hrs | |||
| 加工温度 | 射嘴 | 180-210 | ℃ | ||
| 料筒前段 | 200 | ℃ | |||
| 料筒中段 | 190 | ℃ | |||
| 料筒后段 | 170 | ℃ | |||
| 熔体温度 | ℃ | ||||
| 模具温度 | 60~80 | ℃ | |||
| 压力 | 注塑压力 | 500~1200kg/cm2(7.110~17.070psi) | Mpa | ||
| 保压压力 | 注射压力的50%~100% | Mpa | |||
| 背压 | 5~10kg/cm | Mpa | |||
| 螺杆转速 | 80~120转/分钟 | rpm | |||
| 其他 | 备注 | ||||
| 颜色 | 本白色 | ||||
| 特性 | 低粘度,玻璃珠增强,一般注射成型,它是强化玻璃珠改性牌号 | ||||
| 用途 | 适用于需要低翘曲和下沉现象的部件,具有优良的尺寸稳定性 | ||||